Factory Direct Sales: PP+LGF30 Black Bag/Ton Bag [Color Can Be Customized, Glass Fiber Content 10%-50% Can Be Customized]

Factory Direct Sales: PP+LGF30 Black Bag/Ton Bag [Color Can Be Customized, Glass Fiber Content 10%-50% Can Be Customized]

Factory direct sales, environmentally friendly materials; excellent chemical resistance, excellent dimensional stability;

High strength, high rigidity, high impact resistance, low floating fiber and low density, can replace steel with plastic; high processing efficiency, easy to form various complex and special-shaped parts

[Color can be customized; glass fiber content 10%-50% can be customized]

PP+LGF30 uses continuous glass fiber as a modifier, and has excellent chemical resistance and dimensional stability. It has high strength, high rigidity, high impact resistance, low floating fiber and low density, and can replace steel with plastic. It has high processing efficiency and is easy to form various complex and special-shaped parts.

Consult

Features Technical Indicators Overall Dimension

Product use
This product complies with the industry specifications for continuous glass fiber reinforced polypropylene and is suitable for the production of injection molded polypropylene structural parts, such as washing machine drums, automotive dashboard frames, sub-dashboard frames, sunroof frames, front-end modules, etc.
Product packaging and storage and transportation requirements
Packaging is ton bags/engineering bags
The product should be stored in a ventilated and dry warehouse, away from fire sources, prevent direct sunlight, and must not be stacked in the open air. The product must not be exposed to the sun or rain during transportation, and must not be mixed with sand, broken metal, coal, glass, etc., and must not be mixed with toxic substances, corrosive and flammable items.

Typical performance index (Non Warranted Values)

Test items	Quality indicators	Test results	Test methods
Shrinkage, %	0.4-0.8	0.5	ISO 294
Density, g/cm3	1. 13±0 .02	1.14	ISO 1183
Ash content (mass fraction), %	30±2	29	ISO 3451-1
Tensile strength, MPa	≥130	143	ISO 527
Elongation at break, MPa	≥2.5	2.6	ISO 527
Bending strength, MPa	≥160	180	ISO 178
Flexural modulus, MPa	≥6200	6400	ISO 178
Simple supported beam notched impact strength (acA) 23℃, kJ/m²	≥23	27	ISO 179-1eA
Thermal denaturation temperature (acA) 0.45MPa, ℃	≥158	163	ISO 75
Horizontal combustion (acA) 3.0mm, mm	≤70	28	UL-94

Note: The data in this table are typical values of product performance and are for reference only. For actual data, please refer to the "Quality Inspection Report"
Processing parameters (for reference only)

Drying Temperature	80～ 100℃

Drying Time	2～4h

Rear Temperature	190～210℃

Middle Temperature	210～230℃

Front Temperature	230～245℃

Nozzle Temperature	230～245℃

Melt Temperature	230～245℃

Mold Temperature	60～ 80℃

Injection pressure	70～ 100MPa

Back pressure	0～ 5MPa

Screw Speed	20～ 100rpm